Jesmonite AC100 Kit 35kg is a professional-grade water-based composite material designed for high-quality casting, molding, and surface coating applications. Widely trusted by artists, manufacturers, and designers, Jesmonite AC100 Kit 35kg delivers exceptional strength, fine surface detail, and long-lasting durability while remaining environmentally friendly.
This advanced acrylic-modified gypsum system is ideal for producing decorative panels, architectural moldings, planters, trays, sculptures, candle holders, and bespoke home décor pieces. Unlike traditional resin systems, Jesmonite AC100 Kit 35kg is solvent-free, low-odor, and safer to use indoors, making it perfect for studios, workshops, and commercial production environments.
The bagged base format ensures easy storage and efficient mixing when combined with Jesmonite AC100 liquid. Once mixed, the material offers excellent flow properties, allowing it to capture intricate mold details with precision. It cures quickly to a smooth, stone-like finish that can be sanded, polished, painted, or sealed to achieve a wide range of creative effects.
Jesmonite AC100 Kit 35kg supports pigmentation, terrazzo effects, marble finishes, and reinforcement with fiberglass for enhanced structural strength. Its fire-resistant and impact-resistant properties make it suitable for both decorative and functional applications, including interior design elements and retail display components.
Whether you are scaling production or creating premium handcrafted items, Jesmonite AC100 Kit 35kg provides consistent performance, professional results, and unmatched versatility. It is the preferred choice for makers who demand reliability, sustainability, and superior finish quality in every project.
———————————————————————————————————————————————————————————————————————————
Jesmonite AC100 Kit – 35kg (Bagged Base)
Jesmonite AC100 5kg liquid in Dubai for décor and craft projects.
Jesmonite AC100 is a water-based composite material used to make decorative molded objects. It is safe to use and contains no solvents or VOCs. It can be cast and laminated using our unique Quad axial Glass.
Jesmonite AC100 Liquid should be used within twelve months and Jesmonite Base should be used within nine months from the date displayed on the packaging.
Products benefits
- Superior cast and glass-reinforced moldings
- Solvent free & no VOCs
- Fire resistant
- Lightweight
- Impact resistant
Information
- Easy to use, adaptable material for all molding applications.
- Suitable for decorative cast objects, mold cases, wall panels.
- Supplied with a range of ancillary products including glass reinforcements, pigments, fillers, and control chemicals to adapt the material to the widest range of applications.
- The ultimate chameleon material, can replicate virtually any surface, color, or texture.
SPECIFICATIONS
Mix ratio 2.5:1 parts Base to Liquids ratio by weight
Wet density 1845 kg/m³
Dry density 1745 kg/m³
Initial set 15 – 20 minutes (18°C, No Retarder)
Expansion on set 0.15%
OTHER PROPERTIES
Compressive strength: 25 – 30 MPa
Tensile strength (UTS): 25 – 35 Mpa
Bending elastic limit (LOP): 15 – 20 Mpa
Bending strength (MOR): 50 – 65 Mpa
Youngs Modulus: 5 – 6 Mpa
Impact strength (Charpy): 30 KJ/m²
Moisture movement: <1%
EN13501-1 Fire Classification: B-s1-d0
Freeze/Thaw resistance: Excellent – Test specimens undamaged
Wet/Dry 50 cycles: Test specimens undamaged
APPLICATION AREAS
Cast and laminated decorative moldings, and with the inclusion of suitable glass reinforcements AC100 can be used for lightweight, high-impact panels. Jesmonite AC100 provides a fire resistant coating for many expanded foams for theme park and theatre props.
KEY ATTRIBUTES
Solvent free – No VOC’s
Good abrasion resistance and impact strength
High compressive and tensile strength
Rapid curing and high early strength gain
STORAGE
As a basic rule liquid containers should be kept well sealed to prevent water evaporation and skin forming. They should be stored at a constant temperature between 5 – 25°C and used within twelve months. Freezing must be avoided. Base should be kept dry and stored at 5 – 25°C and used within 9 months.