Jesmonite AC100 Liquid 5kg is a professional-grade water-based acrylic resin liquid designed for high-quality decorative casting, surface coating, and architectural applications. Specially formulated to be mixed with Jesmonite AC100 Base, this advanced liquid system delivers exceptional strength, durability, and smooth surface finishes, making it a preferred choice for artists, designers, and manufacturers worldwide.
The Jesmonite AC100 Liquid 5kg offers excellent adhesion, fast curing time, and low shrinkage, ensuring precise and consistent results across a wide range of creative projects. It is ideal for producing decorative panels, home décor items, sculptures, planters, trays, and architectural mouldings. Its water-based formulation makes it safer to use compared to traditional solvent-based resins, with minimal odor and easy cleanup using water.
This versatile liquid supports pigmentation, terrazzo effects, marbling, and embedded materials, allowing unlimited design creativity. When combined with the AC100 Base, it creates a stone-like, concrete-style finish that is lightweight yet highly durable. The system is suitable for both silicone and rigid moulds, delivering sharp detail reproduction and professional results every time.
Jesmonite AC100 Liquid 5kg is widely used in interior design, commercial projects, workshops, and DIY craft studios. Whether you are creating bespoke décor pieces or producing items at scale, this liquid provides reliable performance, consistent curing, and superior surface quality. Its eco-conscious formulation aligns with modern sustainable crafting practices, making it an excellent choice for responsible creators.
Jesmonite AC100 – 1Kg Liquid
Jesmonite AC100 1kg liquid in Dubai for casting and DIY crafts.
Jesmonite AC100 – 1 kg Liquid
Jesmonite AC100 is a water-based composite material used to make decorative molded objects. It is safe to use and contains no solvents or VOCs. It can be cast and laminated using our unique Quadaxial Glass.
Jesmonite AC100 Liquid should be used within twelve months and Jesmonite Base should be used within nine months from the date displayed on the packaging.
Products benefits
- Superior cast and glass-reinforced moldings
- Solvent-free & no VOCs
- Fire resistant
- Lightweight
- Impact resistant
Information
- Easy to use, adaptable material for all molding applications.
- Suitable for decorative cast objects, mold cases, and wall panels.
- Supplied with a range of ancillary products including glass reinforcements, pigments, fillers, and control chemicals to adapt the material to the widest range of applications.
- The ultimate chameleon material can replicate virtually any surface, color, or texture.
Available in:
Kit sizes range from 3.5kg to 35kg. See the product list for the full range of ancillary materials compatible with AC100.
SPECIFICATIONS
- Mix ratio 2.5:1 parts Base to Liquids ratio by weight
- Wet density 1845 kg/m³
- Dry density 1745 kg/m³
- Initial set 15 – 20 minutes (18°C, No Retarder)
- Expansion on set 0.15%
OTHER PROPERTIES
- Compressive strength: 25 – 30 MPa
- Tensile strength (UTS): 25 – 35 Mpa
- Bending elastic limit (LOP): 15 – 20 Mpa
- Bending strength (MOR): 50 – 65 Mpa
- Youngs Modulus: 5 – 6 Mpa
- Impact strength (Charpy): 30 KJ/m²
- Moisture movement: <1%
- EN13501-1 Fire Classification: B-s1-d0
- Freeze/Thaw resistance: Excellent – Test specimens undamaged
- Wet/Dry 50 cycles: Test specimens undamaged
APPLICATION AREAS
Cast and laminated decorative mouldings, and with the inclusion of suitable glass reinforcements AC100 can be used for lightweight, high-impact panels. Jesmonite AC100 provides a fire resistant coating for many expanded foams for theme park and theatre props.
KEY ATTRIBUTES
- Solvent-free – No VOCs
- Good abrasion resistance and impact strength
- High compressive and tensile strength
- Rapid curing and high early strength gain
STORAGE
As a basic rule liquid containers should be kept well sealed to prevent water evaporation and skin forming. They should be stored at a constant temperature between 5 – 25°C and used within twelve months. Freezing must be avoided. The base should be kept dry and stored at 5 – 25°C and used within 9 months.